Polypropylene (PP) from Kiyanly plant, Turkmenistan

Polypropylene (PP)

Introduction:

Polypropylene (PP) is a thermoplastic “addition polymer” made from the combination of propylene monomers. It is used in a variety of applications to include packaging for consumer products, plastic parts for various industries including the automotive industry, special devices like living hinges, and textiles.

Polypropylene (PP) in Turkmenistan:

Turkmenistan began the sale of polypropylene (PP) and high-density polyethylene (HDPE) from a new gas chemical complex in the village of Kiyanly (Balkan region, Turkmenistan).
The plant will annually process 5 billion cubic meters of natural gas and produce 386,000 tons of polyethylene and 81,000 tons of polypropylene.

Specification and characteristcs of Kiyanly plant (Turkmenistan):

No.

1 2 3 4 5

Product Grade

Injection Molding / Extrusion Film / Extrusion Fiber / Extrusion Yarn / Extrusion Blow Molding / Sheet / Extrusion

Licensor’s Code

L R7175-35.P

L H3066-03.O L H5072-03.O L H5088-25G.O

L H3150-02.O

Remarks R. High Clarity Packaging H. Food Packing /

Non-Food Packing / Non-Packaging,

Film-BOPP

H. Packing, Raffia-Fibre H. Consumer,

BCF/CF

H. Thermoformed sheet, Blow Molding

 


Polypropylene L R7175-35.P
Random Copolymer

Product description and applications:
LR7175-35.P is made via UNIPOL® PP technology, which combines the production efficiency of gas phase fluidized bed reactors with the high activity and stereospecificity of the CONSISTA catalyst system. This product is intended for use in injection molding processes and is recommended for packaging and consumer housewares applications.

 

Features:
LR7175-35.P is designed to provide:
Low taste and odor
Good processibility

 

Typical properties:

Property SI

units

Traditional

units

ASTM

test method

Melt flow rate, (230 °C / 2.16 g) 35 dg/min 35 g/10 min D 1238
Density 0.902 g/cm3 56.31 lbs/ft3 D 792
Tensile yield strength, at 50 mm/min 28 MPa 4060psi D 6381
Tensile elongation at yield, at 50 mm/min 8.00% 8.00% D 6381
Flexural modules (1% secant), at 1.3 mm/min 1100 MPa 159,500 psi D 790A1
Notched Izod impact strength, at 23°C 38 J/m 0.7 ft.lb/in D 2561

 


Polypropylene L H5088-25G.O
Homopolymer

Product description and applications:

L H5088-25G.O is made via UNIPOL® PP technology, which combines the production efficiency of gas phase fluidized bed reactors with the high activity and stereospecificity of the CONSISTA catalyst system. This product is intended for use in bulk continuous fiber processes, from hich fibers are used to produce face yarn for carpet.

Features:

L H5088-25G.O is designed to provide:

Consistent processibility
Anti-gas fading properties
High speed processing
High strength properties

Typical properties:

Property SI

units

Traditional

units

ASTM

test method

Melt flow rate, (230 °C / 2.16 g) 25 dg/min 25 g/10 min D 1238
Density 0.902 g/cm3 56.31 lbs/ft3 D 792
Tensile yield strength, at 50 mm/min 35 MPa 5075 psi D 6381
Tensile elongation at yield, at 50 mm/min 7.00% 7.00% D 6381
Flexural modules (1% secant), at 1.3 mm/min 1480 MPa 214,600 psi D 790A1
Notched Izod impact strength, at 23°C 24 J/m 0.45 ft.lb/in D 2561

 


Polypropylene L H5072-03.O
Homopolymer

Product description and applications:

L H5072-03.O is made via UNIPOL® PP technology, which combines the production efficiency of gas phase fluidized bed reactors with the high activity and stereospecificity of the CONSISTA catalyst system. This product is intended for use in stretched tape (raffia) processes, from which the raffia is used to produce woven fabrics for carpet backing, sacking, industrial, geotextile, and rope and twine applications.

Features:

L H5072-03.O is designed to provide:
Consistent processibility
Good color stability
Low water “carry-over”
High speed processing
High strength properties

Typical properties:

Property SI

units

Traditional

units

ASTM

test method

Melt flow rate, (230 °C / 2.16 g) 3.5 dg/min 3.5 g/10 min D 1238
Density 0.902 g/cm3 56.31 lbs/ft3 D 792
Tensile yield strength, at 50 mm/min 35 MPa 5075 psi D 6381
Tensile elongation at yield, at 50 mm/min 8.00% 8.00% D 6381
Flexural modules (1% secant), at 1.3 mm/min 1500 MPa 217,500 psi D 790A1
Notched Izod impact strength, at 23°C 40 J/m 0.75 ft.lb/in D 2561

Polypropylene L H3066-03.O
Homopolymer

 

Product description and applications:

L H3066-03.O is made via UNIPOL® PP technology, which combines the production efficiency of gas phase fluidized bed reactors with the high activity and stereospecificity of the CONSISTA catalyst system. This product is intended for use in biaxially oriented (BOPP) processes and is recommended as a resin for snack/bakery laminations and overwrap or metallized film applications.

Features:

L H3066-03.O is designed to provide:
Consistent processibility
Good optical properties
High strength properties

 

Typical properties:

Property SI

units

Traditional

units

ASTM

test method

Melt flow rate, (230 °C / 2.16 g) 3.4 dg/min 3.4 g/10 min D 1238
Density 0.902 g/cm3 56.31 lbs/ft3 D 792
Tensile yield strength, at 50 mm/min 32 MPa 4640 psi D 6381
Tensile elongation at yield, at 50 mm/min 9.00% 9.00% D 6381
Flexural modules (1% secant), at 1.3 mm/min 1400 MPa 203,000 psi D 790A1
Notched Izod impact strength, at 23°C 50 J/m 0.9 ft.lb/in D 2561

 


Polypropylene L H3150-02.O
Homopolymer

Product description and applications:

L H3150-02.O is made via UNIPOL® PP technology, which combines the production efficiency of gas phase fluidized bed reactors with the high activity and stereospecificity of the CONSISTA catalyst system. This product is intended for use in extrusion thermoforming and extrusion blow molding processes for applications in packaging.

Features:
L H3150-02.O is designed to provide:
Consistent processibility
Good melt strength
High stiffness
High strength properties

Typical properties:

Property SI

units

Traditional

units

ASTM

test method

Melt flow rate, (230 °C / 2.16 g) 2.5 dg/min 2.5 g/10 min D 1238
Density 0.902 g/cm3 56.31 lbs/ft3 D 792
Tensile yield strength, at 50 mm/min 35 MPa 5075 psi D 6381
Tensile elongation at yield, at 50 mm/min 8.00% 8.00% D 6381
Flexural modules (1% secant), at 1.3 mm/min 1600 MPa 232,000 psi D 790A1
Notched Izod impact strength, at 23°C 45 J/m 0.8 ft.lb/in D 2561

 

Download polypropylene (pp) characteristics and specifications:

 